        • Product Name: GRC Mould Making Silicone Rubber
        • Product No.: HY-635 GRC mould silicone rubber
        • Brand: Hong Ye Silicone
        • Product Usage: mould duplication of GRC prodcuts, cement, concrete, plaster cement and resin products
        • Commodity price: discuss personally
        • Views : 3017

        GRC MOULD MAKING SILICONE RUBBER DESCRIPTION:(link)

        HY-635 casting silicone is mainly used for GRC products molds with the advantages of high tear strength, high durability, high temperature resistance, long shelf life, high duplication times etc. It is suitable for large products or simple products or hard products. This molding silicone is one of the products with the highest use level in the production of many kinds of products, and the shrinkage is even lower than 2‰.The rtv mold making silicone rubber(condensation curing) is generally called two-component room temperature vulcanization type with excellent fluidity and operational performance. Add curing agent of 2%-5% at room temperature, the plaster molding silicone is still operational within 30-60 minutes,and in 2-5 hours, a high tear silicone elastomers will be obtained with resistance to deformation, high-temperature, acid and alkali, and expansion. 

         

        GRC MOULD MAKING SILICONE RUBBER APPLICATIONS:

        This high tear strentgh silicone rubber can be used in making molds for plaster cement, concrete, polyurethaneresin buddha, clay figurine, stone figures, garden sculptures, fiberglass animal, flower pot, fountain, mud decorations, rockery, artificial hill and so on.

         

        GRC MOULD MAKING SILICONE RUBBER OPERATION INSTRUCTION:

        RTV-2 silicone rubber is a flowing liquid with general hardness of 33—37A°after curing process, is in white color. Also you can add some dye according to your needs, but you should contact with us first, because some type of dye will affect the silicone property and quality. If customer wants to make large products and large size molds, the mold should be made of silicone rubber with high hardness such as HY-635 which has 35 shore A hardness. On the contrary, if  the mold with fine and precision patterns, it should be made of silicone with low hardness such as HY-615 which has 15 shore A hardness. The amount of the curing agent depends on the actual requirements of the customer. If requires faster drying rate, more curing agent should be needed; contrarily, if requires slower drying, less curing agent is needed. If all the operation is correct, you will obtain a perfect silicone elastomers for molding. The operation is not difficult, our salesmen can give tailored molding scheme for customers.(every salesmen of Hong Ye Company is well trained to provide with related technical consultation)

         

        The proportions and reactions of the curing agent and the silicone are listed as follows:

          1. Adding curing agent 1%, the silicone could still be operated within 2.5 hours, and could be demoulded after 6-8 hours.

          2. Adding curing agent 2%, the silicone could still be operated within 50 minutes to 1 hour and could be demoulded after 2-3 hours.

          3. Adding curing agent 3%, the silicone could still be operated within 28 - 30 minutes and could be demoulded after 1.5-2 hours.

          4. Adding curing agent 4%, the silicone could still be operated within 10 - 15 minutes and could be demoulded after 1 -1.5 hours.
         

         

        GRC MOULD MAKING SILICONE RUBBER PACKAGE:
        25KG/drum vacuum packing for part A +1kg/ bottle catalyst for part B
        200KG/drum packing for part A +1kg/ bottle catalyst for part B

        Note: 1kg/jar, 5kgs/drum, 20kgs/drum, 25kgs/drum, 200kgs/drum and vacuum package is available.

         

        GRC MOULD MAKING SILICONE RUBBER SHELF LIFE :
        Twelve(12) months when stored under dry and cool place by original package under 25℃

         

        GRC MOULD MAKING SILICONE RUBBER DATASHEET:

        Model

        Appearance

        Viscosity(cps)

        Hardness (A°)

        Tensile Strength (Mpa)

        Tear Strength (KN/m)

        Elongation (%)

        Mixing ratio(%)

        Operating Time(min)

        Curing Time(H)

          HY-635

           White

        27000+5000

        /-8000

            35±2

        5.3

        29

             ≥200

            2~5

           30-40

          4~5

         

         

         

         

         

         

        Note: Above technical datasheet of good tear strength silicone rubber HY-635 is not the fixed  parameters, it's adjustable according to customer's requirements.

        GRC MOULD MAKING SILICONE RUBBER DATASHEET:

        Model

        Appearance

        Viscosity(cps)

        Hardness (A°)

        Tensile Strength (Mpa)

        Tear Strength (KN/m)

        Elongation (%)

        Mixing ratio(%)

        Operating Time(min)

        Curing Time(H)

          HY-635

           White

        27000+5000

        /-8000

            35±2

        5.3

        29

             ≥200

            2~5

           30-40

          4~5

         

         

         

         

         

         

        Note: Above technical datasheet of good tear strength silicone rubber HY-635 is not the fixed  parameters, it's adjustable according to customer's requirements.