        Your present location:Homesilicone productsProductsMold Making Silicone RubberSoap mold silicone > Soap Mold Siline Rubber
        • Product Name: Soap Mold Siline Rubber
        • Product No.: HY-E620 silicone
        • Brand: Hong Ye Silicone
        • Product Usage: Soap mold silicone rubber is suitable for soap,toilet soap,handmade soap mold making. And also inten
        • Commodity price: Discuss personally
        • Views : 330

        Soap Mold Silicone Rubber Description:

          Soap mold silicone rubber is a kind of liquid silicone rubber,which is made up of part A and part B fluidity liquid silicone.It can be cured at room temperature or cured by heating.The mixing ratio of condensation cure silicone rubber is 100:5,and the addition cure is 1:1 or 10:1, these two silicone rubber are suitable to make soap mould.

         

        Soap Mold Silicone Rubber Application

        It has better fluidity performance in RTV-2 mold silicone rubber that is very suitable for soap,toilet soap,handmade soap mold making. And also intended for crafts material mold replication,such as simulated crafts,toys,poly crafts,resin crafts,decoration,furniture ornaments,garden ornaments,garden sculptures and so on.

         

        Soap Mold Silicone Rubber Features:

        1.Not limited by thickness of products,solidified deeply.

        2.Good fluidity,high temperature resistance and thermal stability,suitable for pouring,but if adding special reagent,it can use to brush.

        3.Good chemical-resistance,high and low temperature can reach -50-250℃.

        4.Low line shrinkage.(addition cure silicone rubber is under 0.1%,condensation cure silicone rubber is under 0.3%)  the low molecule is not released during the cross-linking process,so the volume is constant.

        5.High tension and tear strength, long-term no transformation,high duplication times and can reach thousands of times.

        6.Can be cured at room-temperature or cured by heating,easy to operate.

        7.The color,viscosity,hardness and curing time of silicone rubber are adjustable on the basis of your requirements.

         

        Soap Mold Silicone Rubber Operations:

          If your purchase is addition cure silicone rubber,mix part A and part B evenly as 1:1 ratio,if condensation cure silicone rubber,mix part A and part B evenly as 100:5,then putting the mixture into the vacuum machine for eliminating the air,the operation time(normally in 20-60 minutes) depends on temperature,the curing time is in 2-3 hours at room-temperature,and the silicone can be cured in 10 minutes at 80 to 120 ℃.

         

        Soap Mold Silicone Rubber Datasheet of HY-E620:

         

        Model

        HY-E620

        Appearance

        Liquid

        Hardness(shore A)

        20±2

        Mixing ratio(%)

        1:1

        Viscosity(mPa.s)

        7000±2000

        Shrinkage rate(%)

        0.1

        Tensile strength(MPa)

        4.7

        Tear strength(kN/m)

        14±2

        Elongation(%)

        520

        Operation time(mins)

        20-40

        Curing time(hrs 25℃)

        3-5

         

        Soap Mold Silicone Rubber Notes:

        1.If your purchase is addition cure silicone rubber,do not smoke when you are operating the silicone to avoid uncured problem or nonuniform solidification.

        2.HY-E620 silicone is a kind of liquid addition cure silicone rubber,part B is platinum catalyst,the water,impurities,organic bismuth catalyst,acid,alkali and other contain N,P,S organic may influence the silicone be cured,so can not mix these substances when you use the silicone.

        3.No matter what your purchase is addition cure silicone rubber or condensation cure silicone rubber,please putting into mass production after the silicone mould finished in 24 hours later to prolong the working life of moulds.

        Soap Mold Silicone Rubber Datasheet of HY-E620:

         

        Model

        HY-E620

        Appearance

        Liquid

        Hardness(shore A)

        20±2

        Mixing ratio(%)

        1:1

        Viscosity(mPa.s)

        7000±2000

        Shrinkage rate(%)

        0.1

        Tensile strength(MPa)

        4.7

        Tear strength(kN/m)

        14±2

        Elongation(%)

        520

        Operation time(mins)

        20-40

        Curing time(hrs 25℃)

        3-5

         