        Your present location:Homesilicone productsProductsEncapsulant Potting Silicone Rubber > Silicone encapsulant for leds
        • Product Name: Silicone encapsulant for leds
        • Product No.: HY-210
        • Brand: HY silicone
        • Product Usage: Filling for leds, electronic display, circuit board, solar panels, pv cells,machinery
        • Commodity price:
        • Views : 2133

         

        DESCRIPTION OF SILICONE ENCAPSULANT FOR LEDS: (LINK)

        HY210 is a type of two-component encapsulation silicone cured at room temperature.HY 210 works on the surface ofmaterial as PC(Poly-carbonate),ABS,PP,PVC as to its superior bonding feature. It is also applicable for insulation, waterproof and bonding of electronics parts. It has many merits, such as chemical resistance, good thermal transfering ability,  and it meets the requirements of European ROHs, UL94-V1. Hong Ye Technology is one of the best silicone rubber suppliers in China.

         

        USAGE OF SILICONE ENCAPSULANT FOR LEDS:    

        Filling for leds, electronic display, circuit board, solar panels, pv cells,machinery,electrical connections

         

        TECHNICAL GUIDELINES OF SILICONE ENCAPSULANT FOR LEDS:    

               1.Please put part A and B in separate container and stir evenly before mixing the two parts together.
               2. Weight Ratio: part A: part B = 10:1
               3.Bubble release if necessary , deaeration the mixture under 0.08 MPa for 3 minutes.
               4. HY 210 is cured at room temperature, so please put it under room temperature after pouring. It comes to

               next process when basically cured, and it takes about 24 hours for completely cured.

               Kindly note: Temperature and Humidity with tremendous influences for curing of HY210.

         

        WARM TIPS OF SILICONE ENCAPSULANT FOR LEDS:  

                1.Sealing package for storage. The mixture should be used up at once to avoid wasting.
                2. The thermal transfer silicone belongs to non-dangerous goods, but keeps away form mouth and eyes.
                3. When it gets stratified after a period of storage, Please mix HY 210 evenly before using, it does not affect the performance. 

         

        PACKAGE OF SILICONE ENCAPSULANT FOR LEDS:        
                HY210: 22kg/set (Part A 20kg + Part B 2kg)

         

        USAGESHELF LIFE AND TRANSPORTATION OF SILICONE ENCAPSULANT FOR LEDS:    

               1.Twelve(12) months when stored at 24℃ in original unopened packages.
               2. This kind of product is non-dangerous product, it can be transported
        as general chemicals.

               3. Products exceed the storage life should be confirmed normal before using.

         

           If you have any interest or need more information, welcome to contact now:

          Hotline: 86-755-89948019   

                       86-755-89948006

                       86-755-89948294       

         

          E-mail: info@szrl.net              Skype:taylordl828

        TECHNICAL PARAMETERS OF SILICONE ENCAPSULANT FOR LEDS:    

        Properties index

        Part A

        Part B

        Before Curing

         

        Appearance

        Transparent liquid

        yellowish fluid

        Viscosity(cps

        1800±800

        Features when operation

        Mixing Ratio(By weight)

        101

        Operating Time(25℃ /min

        60~120

        Curing time(hrs,basically cured)

        3

        Curing time(hrs,perfectly cured)

        24

        Hardness (shore A)

        15±3

         

        After Curing

        Thermal Conductivity[Wm·K]

        ≥0.2

        Dielectric Strength(kV/mm

        ≥25

        Dielectric permittivity(1.2MHz

        3.03.3

        Volume resistivity(Ω·cm

        ≥1.0×1016

        Fire Resistance

        UL94-V0

        (Please note: all data of this product above in 25 with 55% humidity conditions. We don' t guarantee a same 

        date if testing under different conditions, or when data was regenerated)